IEC 61249-2-45-2018
印制板和其他互連結構用材料. 第2 - 45部分:覆層和未覆層增強基材. 非鹵化環氧化物無紡/機織E -玻璃增強層壓板,導熱率為1.0w / (m - K),并具有規定的可燃性(垂直燃燒試驗),無鉛裝配用銅覆層

Materials for printed boards and other interconnecting structures - Part 2-45: Reinforced base materials clad and unclad - Non-halogenated epoxide non-woven/woven E-glass reinforced laminate sheets of thermal conductivity 1,0 W/(m-K) and defined flammabil

IEC 61249-2-45-2018 發布歷史

This part of IEC 61249 gives requirements for properties of non-halogenated epoxide non-woven reinforced core/woven E-glass reinforced surface laminate sheets of thermal conductivity and defined flammability (vertical burning test), copper-clad for lead-free assembly in thicknesses of 0,60 mm up to 1,70 mm. The flammability rating is achieved through the use of non-halogenated fire retardants reacted as part of the epoxide polymeric structure. The glass transition temperature is defined to be 105 °C minimum. Thermal conductivity is defined to be (1,0 ± 0,15) W/(m-K).

IEC 61249-2-45-2018由國際電工委員會 IX-IEC 發布于 2018-01-00。

IEC 61249-2-45-2018 在中國標準分類中歸屬于: L30 印制電路，在國際標準分類中歸屬于: 13.220.40 材料和制品的可燃性和燃燒性能,31.180 印制電路和印制電路板。

IEC 61249-2-45-2018 發布之時，引用了標準

• IEC 61189-2-2006 電氣材料、互連結構和組件的試驗方法.第2部分:互連結構用材料的試驗方法
• IEC 61249-5-1-1995 互連結構用材料 第5部分:有或無涂層的導電箔和薄膜分規范集 第1節:銅箔(用于生產覆銅基材)
• IEC/PAS 61249-6-3-2011 印制板用電子級玻璃纖維制成的成品布織物規范
• ISO 11014-2009 化學產品的安全數據單.內容和數據項順序

IEC 61249-2-45-2018的歷代版本如下：

• 2018年01月 IEC 61249-2-45-2018 印制板和其他互連結構用材料. 第2 - 45部分:覆層和未覆層增強基材. 非鹵化環氧化物無紡/機織E -玻璃增強層壓板,導熱率為1.0w / (m - K),并具有規定的可燃性(垂直燃燒試驗),無鉛裝配用銅覆層

標準號

IEC 61249-2-45-2018

發布日期

2018年01月

實施日期

廢止日期

無

中國標準分類號

L30

國際標準分類號

13.220.40;31.180

發布單位

國際電工委員會

引用標準

IEC 61189-2-2006 IEC 61249-5-1-1995 IEC/PAS 61249-6-3-2011 ISO 11014-2009

被代替標準

IEC 91/1447/CDV-2017

適用范圍

This part of IEC 61249 gives requirements for properties of non-halogenated epoxide non-woven reinforced core/woven E-glass reinforced surface laminate sheets of thermal conductivity and defined flammability (vertical burning test), copper-clad for lead-free assembly in thicknesses of 0,60 mm up to 1,70 mm. The flammability rating is achieved through the use of non-halogenated fire retardants reacted as part of the epoxide polymeric structure. The glass transition temperature is defined to be 105 °C minimum. Thermal conductivity is defined to be (1,0 ± 0,15) W/(m-K).